0.18-0.25MM CERAMIC SAND B80
Ceramic sand is an ideal sand blasting material with imported zircon sand as raw material, melting above 2000 degrees, injection cooling, particle size classification and removal of magnetic and non-magnetic impurities.
CHEMICAL COMPOSTION%
| ZrO2 | SiO2 | Al2O3 |
| 60-70% | 28-33% | < 10 % |
PHYSICAL PROPERTIES
| Specific Gravity | Bulk Density | Hardness |
| ＞3.85g/cm3 | ＞2.30g/cm3 | 700（HV0） 7 （F. Mons） 60HRC（HR） |
0.18-0.25MM CERAMIC SAND B80 PARTICLE SIZE DISTRIBUTION
| SIZE | SIZE RANGE/mm | PARTICLE SIZE DISTRIBUTION | |
|
B80 |
0.18-0.25mm |
0.250-0.300mm | ＜10% |
| 0.180-0.250mm | 85-100% | ||
| 0.125-0.18mm | ＜10% | ||
MAIN APPLICATIONS OF CERAMIC SAND
–Medical treatment: surface treatment such as deburring of stainless steel surgical instruments and titanium alloy human implanted devices.
–High iron field: it can be used for sandblasting the surface of high iron aluminum alloy parts to improve the metal texture and form a smooth satin effect. Used for grinding and finishing of high-speed rail.
— Automotive field: ceramic shot can be used for surface cleaning and deburring of Automotive Engine Castings; It is used to clean the welds and welding spots on the car floor and prepare for subsequent spraying;
–Mold and machining: used for sand blasting of stainless steel mold, copper mold and aluminum alloy mold, such as tire mold, injection mold and stamping mold, to improve surface finish. Clean the flash and burr of machined parts.
–Electronic equipment field: ceramic shot is used for sandblasting the shells of mobile phones, tablet computers and watches made of aluminum alloy or stainless steel.
— Kitchen utensils industry: it is used for sandblasting of high-quality stainless steel cookware, pot bottom, soup spoon and other products, giving the products delicate metal texture and certain antibacterial ability.
–Glass products industry: used for automization treatment of glass, replacing hydrofluoric acid chemical etching process to prevent pollution.
–Shot peening of aviation parts: used to improve the fatigue resistance of carbon steel, titanium alloy, aluminum alloy and other aviation mechanical parts and eliminate surface stress.
…
AVAILABLE SIZES
B20 B30 B40 B60 B80 B100 B120 B125 B150 B170 B205 B400 B505